Νέες Τεχνολογίες και Εφαρμογές Υλικών Πολυουρεθάνης και Προϊόντων Πολυουρεθάνης

Πολυουρεθάνηmaterials [that is, high molecular polymers containing urethane groups and -NHCOO in the main chain of macromolecules] have developed rapidly since the industrial production was not released on the market in the 1950s. Compared with polymer rubber materials, it has its own unique characteristics. It can use different numbers of functional groups and different types of functional groups according to different performance requirements, and use different production processes to produce πολυουρεθάνη products with different properties and properties.

Among rubber rubber types, there are πολυουρεθάνη rubber varieties that can be cross-linked. There are also those that are not in the category of rubber, such as foam plastics, rigid plastic products, coatings, high resilience synthetic fibers, artificial leather, adhesives, and so on.

Τα υλικά πολυουρεθάνης χρησιμοποιούνται σήμερα ευρέως σε διάφορους τομείς. Για παράδειγμα, στη αεροδιαστημική βιομηχανία, τα σκληρά προϊόντα, τα μαλακά προϊόντα και τα προϊόντα αφρού είναι ελαφρύτερα από τα μεταλλικά υλικά, [πολύ σημαντικά για τα αεροσκάφη] και έχουν υψηλή ανθεκτικότητα και μη ευφλεκτότητα. , Μόνωση υψηλής αντοχής, εξαιρετικά χαμηλής θερμοκρασίας κ.λπ., που χρησιμοποιείται για κουκούλες αεροσκαφών, φρένα ταχύτητας, ραδόμυλα, υλικά πλήρωσης δεξαμενών καυσίμου αεροσκαφών, σημαδούρες ατμοποιητή ελέγχου κατανάλωσης καυσίμου κ.λπ., καθώς και διάφορα πλαίσια στήριξης και μαξιλάρια καθισμάτων για εσωτερική διακόσμηση Ε Χρησιμοποιείται για τη διατήρηση της θερμότητας στη βιομηχανία μεταφορών.Πολυουρεθάνητα υλικά είναι αδιαχώριστα από υλικά και μαξιλάρια καθισμάτων, την κατασκευή επίπλων σπιτιού, ακόμη και προφυλακτικά για ενήλικες υψηλών προδιαγραφών και ελαστικά. Και η πρόσφατη ανάπτυξη και χρήση προϊόντων σε αξεσουάρ απορρόφησης και απόσβεσης αυτοκινήτων έχουν προσελκύσει περισσότερη προσοχή.

Although there are many types of πολυουρεθάνη products, the classification of its products is nothing more than:

Flexible foam products, rigid products, and elastomers [thermoplastic elastomers, vulcanizable elastomers EU, AU]. The product molding equipment, such as mixing πολυουρεθάνη rubber, is generally solid and can be vulcanized with sulfur, peroxide, and polyisocyanate. It can be designed according to the conventional rubber product production process and formula. If it is a thermoplastic elastomer, it can be injection or compression molding. If it is a plastic πολυουρεθάνη, μπορεί να παραχθεί με μέθοδο χύτευσης. Λήψη ευέλικτουπολυουρεθάνη foam products as an example, the composition of the formula, the main reactants of which are polyether, polyester, or other polyols; and polyisocyanates. Others include water [chain extender], crosslinking agent, catalyst, foam stabilizer, external blowing agent, flame retardant, mold release agent, coloring agent, etc. The production process is generally two-component liquid reaction molding. That is to say, one group is that the polyol polymer and the isocyanate are mixed and reacted first, and then the above reactants are mixed with another group including water, blowing agent, stabilizer, catalyst, and various auxiliary agents to produce organic carbamate. At the same time, the reactants such as urea group use the reaction to generate carbon dioxide, release a large amount of heat, vaporize the added blowing agent, and then use the catalyst to adjust the foaming speed, and finally complete the product with uniform foam structure. At present, the automobile manufacturing industry has continuously improved safety, comfort, and durability, and has high requirements for durability in high-strength working conditions of shock-absorbing and damping elastomer parts. A new type of shock absorber made of πολυουρεθάνη flexible foam has appeared in foreign markets. Its physical and mechanical properties and damping effect are slightly better than rubber damping accessories. The product requires a density of 0.08g 丿cm3, a material compression of 5%, a compressive strength of more than 7Kpa, the product works normally at -20-40 "degrees", the product's compression set is not more than 10%, and it has oil resistance. Under pressure impact, no fracture occurs. The production process is not special. The key lies in its main reaction material. Currently, BASF is monopolizing the production and supply. BASF also learns from DuPont's market supply principle of perfluoroether rubber, which is to sell only finished products, not raw materials. , In order to achieve the reduction of market competitors.

Αυτός ο νέος τύποςπολυουρεθάνηΤα εύκαμπτα αφρώδη εξαρτήματα απορρόφησης κραδασμών αυτοκινήτων υιοθετούν μια προηγμένη διαδικασία χύτευσης "ενός σταδίου", δηλαδή όλα τα συστατικά των πρώτων υλών στη σύνθεση, όπως ισοκυανικό, πολυμερές πολυόλης, επέκταση αλυσίδας, καταλύτης, σταθεροποιητής αφρού και άλλα Ο βοηθητικός παράγοντας μετριέται σύμφωνα με τον τύπο, με το ισοκυανικό ως ξεχωριστό συστατικό, και διάφοροι βοηθητικοί παράγοντες όπως πολυμερές πολυόλης, νερό, βοηθητικός παράγοντας εμφύσησης, επέκταση αλυσίδας, επιφανειοδραστική ουσία, καταλύτης κ.λπ. προετοιμάζονται εκ των προτέρων σε ένα συστατικό και στη συνέχεια μία φορά Προσθήκη στη δεξαμενή αντίδρασης και στη συνέχεια προσθέστε τον παράγοντα αφρισμού. Μετά από ανάδευση και ανάμιξη υψηλής ταχύτητας, πραγματοποιείται η διαδικασία αντίδρασης αφρισμού. Αυτή η διαδικασία παραγωγής ενός σταδίου είναι ιδιαίτερα κατάλληλη για την επεξεργασία αξεσουάρ με πολύπλοκα σχήματα και μικρές προδιαγραφές. Στη μέθοδο χύτευσης, το αναμεμιγμένο υγρό εγχέεται απευθείας σε ένα καλούπι με περίπλοκο σχήμα και στη συνέχεια αφρίζεται στην κοιλότητα του καλουπιού για σχηματισμό. Προϊόντα που κατασκευάζονται με αυτή τη μέθοδο. Οι προδιαγραφές και οι διαστάσεις είναι ακριβείς και μπορεί επίσης να χρησιμοποιηθεί ως μεταλλικά ένθετα προϊόντα ανάλογα με τις ανάγκες.

Πολυουρεθάνηproducts are currently widely used and the market demand is also large. Although my country started late, it has developed rapidly. Its global market share has reached more than a quarter. It has become the world's largest manufacturing and consumer market for πολυουρεθάνη products. However, there is still a gap between the key main reaction materials and the advanced foreign level, and the industry needs to work hard to innovate and develop.It is reported that retreading tires with πολυουρεθάνη material as tread rubber has better wear resistance and environmental protection than natural rubber. This innovative research and development has opened up a new way for retreading. During the "13th Five-Year Plan" period, the πολυουρεθάνη industry will have more room for development.